Eight Locations And Reasons For The Easy Cracking Of Quartz Stone
May 29, 2018

In the purchase of quartz stone countertops, many consumers are blinded by the price, thinking that the quality of quartz stone has little to do with the price. I think I can use it.



The quality of quartz stone itself is on the one hand. In the process of processing and installation, if there is a situation of cutting corners and cutting materials, the process is not rigorous, etc., it is likely that cracking will occur later in the process. For example, the following types:



First, the table joint cracking cracks: the main installation workers in the seam, the seam is not aligned, opened into a small bell above the small, glue is not coated even more important is the glue is not fixed using F clamp, or in Adding curing agent to the glue or promoting overdosing to make the patchwork brittle, and it will be cracked when it is in use.



Second, the corner of the crack: the wall is too tight without leaving the contraction joint, the two cabinets are uneven or unleveled, the front angle turned into a right angle to open into the internal stress concentration, the impact of external forces or temperature changes in the tabletop uneven shrinkage and cracking;



3. Peripheral cracks in the stage basin: No gaps are left between the stage basin and the basin holes, the basin holes are not polished smooth, the four corners of the basin holes are not rounded or saw-tooth marks are left, and the tabletop shrinks unevenly and cracks due to external impact or temperature changes;



Fourth, the crack around the furnace hole: Gas stove and the hole does not leave a gap, the furnace hole is not polished smooth, four corners of the basin hole is not rounded or sawtooth India, by the impact of external forces or temperature changes uneven shrinkage of the tabletop;



5. The skirt on the stage above the basin and the front of the furnace hole is cracked: the cabinet counter or the stove cabinet is placed flat on the counter, and the counter basin, the front skirt of the furnace hole are caused by gravity (person stepping, stepping, etc.), etc. The front skirt cracks;



Sixth, after the water block crack: Cabinet is not flat or pad is not flat;



Seven, after the water side to connect the table surface cracking: adhesive bonding is not strong;



8. Cracking at the center of the table top, etc.: High temperature, impact by external force, unevenness of cabinets or backing plates, internal injuries to the plate, etc.; therefore, the main cause of table cracking is caused by lax quality control of the table top during the processing.


  • Newsletter
  • Categories
  • Contact Us

    Linhai Zhengda Machinery Co.,Ltd
    Add: No.261, Hushan South Road, Xiaozhi Town, Linhai City, Zhejiang Province, China
    Contact: Kevin
    Tel: +86-576-85889981
    Mob: +8613666497878
    E-mail: zhengda@cnzdkj.com

  • QR Code
  • Copyright © Linhai Zhengda Machinery Co.,Ltd All Rights Reserved.